ASTM A Standard Specification for Steel Strip, High Carbon, Cold Rolled, General Requirements. Find the most up-to-date version of ASTM A at Engineering ASTM A, AM – Designation: A /A M – 02 An American National Standard Standard Spe.
|Published (Last):||14 January 2006|
|PDF File Size:||7.50 Mb|
|ePub File Size:||16.68 Mb|
|Price:||Free* [*Free Regsitration Required]|
Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.
This standard has been approved for use by agencies of the Department of Defense. The values listed are not exact conversions of the values listed in the inch-pound tables but instead are rounded or rationalized values.
Conformance to SI tolerances is mandatory when the “M” specification is used. However, under SI the preferred term in mass. NOTE 3—When the camber tolerances shown in Table 8 are not suitable for a particular purpose, cold-rolled strip is sometimes machine straightened. A portion of the coil may be discarded prior to cutting the samples for retest. Within the text, the SI units are shown in brackets.
ASTM A Steel, Strip, High Carbon, Cold Rolled, General Requirements
The values listed are not exact conversions of the values listed in the inch-pound tables but z682 are rounded or rationalized values. NOTE 1—The term weight is used when inch-pound units are the standard.
Two additional samples are secured from each end of the coil from which the original sample was taken. Link to Active This link will always route to the current Active version of the standard.
Note 1—The term weight is used when inch-pound units asm the standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. If any of the retests fail to comply with the requirements, the coil shall be rejected.
Combining values from the two systems will result in nonconformance with the specification. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other.
Normal coiling or piling does not asrm a 3 Where an ellipsis. Revision to Table 2. Combining values from the two systems will result in nonconformance with the specification. However, unless the order specifies the applicable “M” specification designation SI unitsthe material shall be furnished to inch-pound units. Strip is classified as product that is 0. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every? The results of analyses taken from different pieces within a heat may differ from each other and from the cast analysis.
Table 3 shows requirements for additional elements.
ASTM A682 Grade 1074
Individual reprints single or multiple copies of this standard may be obtained sstm contacting ASTM a82 the above address or at phonefaxor service astm.
Each of the elements listed in Tables 2 and 3 and additional elements agreed upon by the purchaser and the supplier shall be included in the report of heat analysis.
B Measured 10 mm or more in from edge; and on narrower than 25 mm, at any place between edges.
The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. C Number 3 edge strip with thickness tolerance guaranteed at less than 3?
The strip may be subjected to product analysis by the purchaser either for the purpose of verifying that the chemical composition is within speci? Rework and Retreatment Elements such as aluminum may be added in sufficient amounts to a82 the austenitic grain size.
NOTE 2—Camber tolerances as shown in the table are for any mm length.